Manufacture of Modified Protective Coating for internal surfaces of furnaces(refractory)
عنوان مقاله: Manufacture of Modified Protective Coating for internal surfaces of furnaces(refractory)
شناسه ملی مقاله: KOUREH04_004
منتشر شده در چهارمین کنفرانس مشعل و کوره صنعتی در سال 1393
شناسه ملی مقاله: KOUREH04_004
منتشر شده در چهارمین کنفرانس مشعل و کوره صنعتی در سال 1393
مشخصات نویسندگان مقاله:
Amin Amin ahmadpour - National Petrochemical company-Bandar Imam Petrochemical Company-Research and Technology Center
khashayar shakiby - ham andishan enerjy kimia company
خلاصه مقاله:
Amin Amin ahmadpour - National Petrochemical company-Bandar Imam Petrochemical Company-Research and Technology Center
khashayar shakiby - ham andishan enerjy kimia company
In this work, coal residue (pitch) was used to produce an inexpensive protective coating. The residue is primarily rehabitated for just to be suitable for use as a coating material (reference coat) by dissolving it in benzene in a ratio of Pitch/Solvent(P/S) = 3:1 by weight . The reference coating was then mixed with polyurethane (commercial type) in percentages ranging from 5 to 15 % by weight of the solid tar pitch . Well mature mortar cubes (7x7x7cm) with a (w/c =0.4) and sand-cement (s/c= 2.75)were cast and covered with the prepared coatings. The cubes were then soaked individually in tap water , MgCl2-5% conc. and H2SO4- 3.0% conc. for different periods of time. The last two reagents represent sea water and 5 years complete immersion in sewage water respectively. The effect of reagents on the compressive strength , water retention and weight was measured for the cubes. The results revealed that, all prepared coatings gave satisfied physical characteristics. Addition of PUR up to 10% by weight of coal residue produced coating materials with the most favorable physical and chemical behavior.
کلمات کلیدی: Pitch – Coating – Sea water – mortar- furnace- refractory