Delamination Analysis in Composite Root of a Carbon-Layer Reinforced Wind Turbine Blade
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 296
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_MACS-6-1_002
تاریخ نمایه سازی: 14 تیر 1399
چکیده مقاله:
The inconsistencies accompanied with material properties tipically cause the rise of delamination risk in composites made of different types of glass and crabon fibers. In this study, the delamination of a composite beam reinforced with a carbon layer under bending load is investigated. To this end, a small piece of a wind turbine blade root in the form of a heterogeneous laminated plate is simulated and analyzed. The methodology consists of two parallel approaches, including the experimental measurements and computer simulations. In the experimental program, the delamination of different specimens has been examined by three-point bending (3PB) tests. The diagrams of load versus load line displacement are recorded. In computer simulation, the geometry of composite laminate is re-modeled and stress analysis is performed. The results confirm that delamination loads obtained from the simulations are reliable and in good agreement with those obtained from the experimental procedures. The results of experimental measurements and computational simulations are utilized to predict the delamination failure and to optimize the lay-up sequence of the reinforced structure.
کلیدواژه ها:
نویسندگان
Mohammad Hadi Safari Naderi
Mechanical Engineering Department, Semnan University, Semnan, Iran.
Hamid Ekhteraei Toussi
Mechanical Engineering Department, Faculty of Engineering, Ferdowsi University of Mashhad (FUM).
Ahmad Ghasemi Ghalebahman
Mechanical Engineering Department, Semnan University, Semnan, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :