Preparation of γ-Al۲O۳ and Prioritization of Affecting Factors on the Crystallite Size Using Taguchi Method
سال انتشار: 1392
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 180
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_CHAL-1-1_005
تاریخ نمایه سازی: 2 مرداد 1401
چکیده مقاله:
In this work, boehmite sol was prepared by a previously applied and validated method; hydrolysis of aluminum chloride hexa-hydrate. In order to obtain precise results, the effect of pH after adding precipitating agent, aging time, peptizing temperature and ultrasonic vibration time on the crystallite size of final precipitate were investigated in a narrow range. The preparation conditions applied in the production step of nanocrystalline boehmite affected on the desired alumina phase. Experiments were set based on the statistical design of experiments (Taguchi method). Furthermore the influence of calcination on crystallization and phase transformation of the precipitate was investigated using X-ray diffractometry (XRD) and simultaneous thermal analysis (STA) techniques. To evaluate the results, the obtained data were statistically analyzed. Considering the statisti cal analysis of experiments, the pH after adding precipitating agent is the major parameter affecting crystallite size. In contrast, aging time has the smallest effect on the crystallite size. In addition, Transmission electron microscopy (TEM) of the samples revealed that the particle size of the powders was well distributed in the nano-size range. Taguchi prediction on the crystallite size was ۲.۰۹۶±۰.۱۳۹ nm (with confidence interval of ۹۵%) which confirmed by a verification experiment (۲.۰۶۴ nm).
کلیدواژه ها:
نویسندگان
M. Shayesteh
Deparetment of Chemical Engineering, University of Sistan and Bluchestan, Zahedan, Iran
M. Shafiee Afarani
Department of Materials Engineering, University of Sistan and Bluchestan, Zahedan, Iran
A. Samimi
Deparetment of Chemical Engineering, University of Sistan and Bluchestan, Zahedan, Iran
M. Khorram
Deparetment of Chemical Engineering, University of Sistan and Bluchestan, Zahedan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :