Study of TIG Surface Melting and Molybdenum Surface Alloying of ADI
سال انتشار: 1386
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,897
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICME08_163
تاریخ نمایه سازی: 27 آبان 1388
چکیده مقاله:
In this study the effect of variations of the current intensity and travel speed on the dimensions of the melted and heat affected zones of TIG surface melted and molybdenum surface alloyed samples of ADI was investigated. The results implied the variations of dimensions were more susceptible to the current intensity, and also the width of the molten pool showed higher susceptibility to the increase in heat input than its depth. Besides, molten pools formed by surface alloying were smaller yet deeper than surface melting. Surface melting formed a ledeburitic structure in the resolidified zone with the hardness up to 985 HV, and molybdenum surface alloying resulted in formation of a structure consisting of cementite, martensite, retained austenite and (Fe,Mo)3C carbides with the hardness up to 1055 HV. Surface melting and molybdenum surface alloying also reduced the wear rate of the ADI up to 37% and 62% respectively.
کلیدواژه ها:
نویسندگان
A Amirsadeghi
Graduate student of the University of Tehran
M Heydarzadeh Sohi
Professor of the University of Tehran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :